This study aims to evaluate the influence of different annealing temperatures on the microstructure and mechanical behaviour of C36000 brass. The specimens were heat treated at temperatures ranging from 250°C to 850°C for 1 hour, followed by quenching in water. Afterward, the microstructural and mechanical characterization was performed. The microstructural characterizations reveal that both the as-received specimen and the heat treated specimens exhibit a 𝛼 + 𝛽 microstructure, with a drastic change in the phase fractions observed only for temperatures above 400°C. From a mechanical properties standpoint, there was increase in the mechanical strength with increasing temperature up to 550°C. However, there was a decrease in mechanical strength and an increase in hardness at temperatures above 550°C.
Resumo:
Este estudo tem como objetivo avaliar a influência de diferentes temperaturas de recozimento na microestrutura e no comportamento mecânico do latão C36000. As amostras foram tratadas termicamente em temperaturas variando de 250°C a 850°C por 1 hora, seguidas de resfriamento em água. Em seguida, foi feita a caracterização microestrutural e mecânica. As caracterizações microestruturais revelam que todas as amostras exibem uma microestrutura 𝛼 + 𝛽, com uma mudança drástica nas frações de fase observada apenas para temperaturas acima de 400°C. Do ponto de vista das propriedades mecânicas, houve aumento na resistência mecânica com o aumento da temperatura até 550°C. No entanto, houve uma diminuição na resistência mecânica e um aumento na dureza em temperaturas acima de 550°C.
Referência:
ONISHI, Michelle Midori; DANNINGER, Leonardo Rodrigues; RIOS, Carlos Triveño. Effects of heat treatment temperature on the microstricuture and some mechanical properties of C36000 BRASS. In: CONGRESSO ANUAL DA ABM, 77., 2024, São Paulo. Palestra… 14 slides
Acesso aos slides da apresentação da Palestra em PDF: