Abstract:
Scanning Kelvin probe force microscopy was used to evaluate the effect of austenitisation temperatures during hot stamping on the local electrochemical behaviour of 22MnB5 steel coated with hot-dip Al-Si. A variation in the austenitisation temperature around 50 ◦C substantially altered the coating morphology as well as the local electrochemical behaviour of the system (coating/steel). Both coating layer and steel substrate became nobler as the austenitisation temperature increased. The former was due to the overall iron enrichment while the latter was related to the microstructural transformation during quenching. Therefore, the driving force for cathodic protection decreased as the austenitisation temperature increased.
Reference:
COUTO, Camila Pucci; REVILLA, Reynier I.; POLITANO, Rodolfo; COSTA, Isolda; PANOSSIAN, Zehbour; GRAEVE, Iris De; ROSSI, Jesualdo Luiz; TERRYN, Herman. Influence of austenitisation temperatures during hot stamping on the local electrochemical behaviour of 22MnB5 steel coated with hot-dip Al-Si. Corrosion Science, v.190, 109673, Sept., 2021.
Access to the abstract of the article on the Journal website:
https://www.sciencedirect.com/science/article/abs/pii/S0010938X2100439X?via%3Dihub
Scanning Kelvin probe force microscopy was used to evaluate the effect of austenitisation temperatures during hot stamping on the local electrochemical behaviour of 22MnB5 steel coated with hot-dip Al-Si. A variation in the austenitisation temperature around 50 ◦C substantially altered the coating morphology as well as the local electrochemical behaviour of the system (coating/steel). Both coating layer and steel substrate became nobler as the austenitisation temperature increased. The former was due to the overall iron enrichment while the latter was related to the microstructural transformation during quenching. Therefore, the driving force for cathodic protection decreased as the austenitisation temperature increased.
Reference:
COUTO, Camila Pucci; REVILLA, Reynier I.; POLITANO, Rodolfo; COSTA, Isolda; PANOSSIAN, Zehbour; GRAEVE, Iris De; ROSSI, Jesualdo Luiz; TERRYN, Herman. Influence of austenitisation temperatures during hot stamping on the local electrochemical behaviour of 22MnB5 steel coated with hot-dip Al-Si. Corrosion Science, v.190, 109673, Sept., 2021.
Access to the abstract of the article on the Journal website:
https://www.sciencedirect.com/science/article/abs/pii/S0010938X2100439X?via%3Dihub